Synthesis and Characterization of Super Paramagnetic Iron Oxide Nanoparticles

Background: Iron oxide (γ-Fe2O3) nanoparticles have been prepared by a simplified coprecipitation method. Methods: X-ray diffraction peaks of the prepared nanoparticles match well with the characteristic peaks of crystalline g-Fe2O3 as per JCPDS data (JCPDS Card No. 39-1346) and absorption peak at 369 nm along with band gap 2.10 eV suggesting the formation of (γ-Fe2O3) nanoparticles. Results: The γ-Fe2O3 nanoparticles are spherical in nature with a diameter around ~10 nm. Conclusion: The crystalline g-Fe2O3 nanoparticles exhibit excellent super-paramagnetic behavior not only at room temperature (300K) but also at a temperature as low as 100K.